Single component fire-retardant polyurethane foam PU
JNTFM-FIREPROT-PU-750ML
Register now and access more than 150,000 products
Fire resistant to EI 240
- Can be cut, ground, sanded, painted, perforated and plastered once cured
- High adhesive strength
- Good resistance to water, chemicals, cleaning agents and microorganisms
- Very low emission of volatile organic substances (EC 1 Plus)
- High resistance to fire for up to 240 minutes (depending on the type of application)
- Can be used for any length of joint, both with and without rock wool
- High fire resistance times even in walls only 100 mm thick
- Thanks to its consistency (foam), it adapts to geometries and can be used for joints of various sizes
- Quick application and high yield (1 cylinder = approx. 40 l)
- Easy to extrude using a conventional PU foam gun
Because the material is not intumescent, it is not suitable for the fire-retardant sealing of joints containing pass-through elements (pipes, cables etc.). Use other Fireseal systems
Do not use for sealing flues
Certificates: www.wuerth.it/progettisti
Observe the positioning specifications in each case
| Fire resistance values in accordance with EN13501-2 - wall application | ||||||
| Min. wall thickness/mm | Joint direction | Sample name | Joint width/mm | Thickness of rock wool mm (density ≥ 40 kg/m3) | PU foam thickness/mm | Fire resistance |
| 100 | Vertical | A | 10 | 60 | 20* | EI 180 |
| B | 20 | - | 100 | EI 60 | ||
| Horizontal | F | 10 | - | 100 | EI 120 | |
| G | 20 | 60 | 20* | EI 120 | ||
| 150 | Vertical | C | 30 | - | 150 | EI 60 |
| D | 40 | 100 | 25* | EI 120 | ||
| E | 50 | - | 150 | EI 30 | ||
| Horizontal | H | 30 | 100 | 25* | EI 240 | |
| I | 40 | - | 150 | EI 60 | ||
| L | 50 | 100 | 25* | EI 180 | ||
| *Application on both sides of the wall | ||||||
| Fire resistance values in accordance with EN13501-2 - ceiling application | |||||
| Min. ceiling thickness/mm | Sample name | Joint width mm | Thickness of rock wool mm (density ≥ 40 kg/m3) | PU foam thickness/mm | Fire resistance |
| 150 | A | 10 | 100 | 25* | EI 120 |
| B | 20 | - | 150 | EI 120 | |
| C | 30 | - | 150 | EI 120 | |
| D | 40 | 100 | 25* | EI 240 | |
| E | 50 | - | 150 | EI 60 | |
| F | 60 | - | 150 | EI 45 | |
| G | 70 | 100 | 25* | EI 120 | |
| *Application on both sides of the ceiling | |||||
Datasheets(X)
For fire-retardant sealing of vertical and horizontal linear joints in rigid walls (concrete, aerated concrete and masonry) and rigid floors (concrete and aerated concrete) requiring a degree of fire resistance
Sealing of joints between two walls or floors and also between the wall and frame of fire doors
Other uses (in the absence of specific EI fire resistance requirements):
- Fixing electrical ducts and junction boxes: the foam has passed the glowing-wire resistance test at 850°C according to IEC EN 60695-2-11
- For all common applications of a normal PU foam
Contents | 750 ml |
Chemical basis | Single component polyurethane |
Density | 19 kg/m³ |
Density conditions | at 23°C, 50% relative humidity |
Colour | Grey |
Container | Aerosol can |
Min. joint width | 10 mm |
Max. joint width | 70 mm |
Min. temperature resistance | -40 °C |
Max. temperature resistance | 120 °C |
Min. ambient processing temperature | 5 °C |
Max. ambient processing temperature | 40 °C |
Min. processing temperature | 5 °C |
Max. processing temperature | 40 °C |
Min. surface processing temperature | 5 °C |
Min./max. processing temperature | 5 to 40 °C |
Min./max. processing temperature for can | 5 to 25 °C |
Min. processing temperature for can | 5 °C |
Max. processing temperature for can | 25 °C |
Optimum processing temperature for can | 20 °C |
Min. skin-formation time | 8 min |
Conditions for skin-formation time | at 23°C and 50% relative humidity |
Tensile strength | 12 N/cm² |
Yield (volume) approx. | 40 l |
Conditions for yield | Foam yield (free foaming) |
Yield (volume) approx./conditions | 40 l / Foam yield (free foaming) |
Silicone-free | Yes |
Building material class | B-s2, d0 - Of low flammability |
Building material class conditions | in accordance with DIN EN 13501-1 |
Fire resistance rating | EI120 |
Ultraviolet resistance | No |
Smell/fragrance | Characteristic |
Shelf life from production | 12 Month |
Conditions to maintain shelf life from production | upright, cool and dry storage area |
Weight of content | 794 g |
Product weight (per item) | 1175.000 g |
| Technical data: | |
| Reaction to fire according to EN 13501-1 | Class B-s2, d0 (corresponds to class B1 according to DIN 4102) |
| Density | 19 to 24 kg/m3 |
| Humidification | Dampen the underlying surface when using the product |
| Yield of the freely expanded foam | Approx. 40 l (at +23°C/50 % relative humidity) |
| Curing time = 20 mm bead hardening | Approx. 60 minutes (at +23°C/50 % relative humidity) |
| UV resistance | Low, yellowing likely |
| Adhesion | Excellent, except on polyethylene, PTFE, silicones or other similar materials |