Zinc spray
Zinc spray
ZNSPR-METAL-400ML
Register now and access more than 150,000 products
Excellent corrosion protection
- The metal is actively protected, even with minor damage
- Over 100 hours of salt-spray resistance (DIN 50021 SS)
Excellent adhesive properties on bare metal
Excellent spot welding properties
Not suitable as a primer for PU, MS polymer or hybrid sealing compounds.
Do not paint over with other paints
Datasheets(X)
For visual enhancement, repair and protection against corrosion of metallic surfaces.
The optimal application temperature is between 15°C-25°C
Contents | 400 ml |
Chemical basis | Nitroalkydale |
Colour | Zinc, bright |
Min. curing time | 1 h |
Fully hardening/curing conditions | 20°C |
Max. curing time | 1 h |
Resistance in salt-spray test | 500 h |
Max. temperature resistance | 200 °C |
Dust-drying time | 10 min |
Dry layer thickness (first back-and-forth motion) | 50 µm |
Conditions for dust-drying time | at 20°C |
Zinc content in the dry film | 91.55 % |
Zinc content in the paint | 65 % |
Zinc content in the pigment | 99.9 % |
Coating thickness | 50 µm |
Recoatable/Can be painted over | Yes |
Grip strength conditions | at 20°C |
Substrates with good adhesion | Steel |
Spot weldable | 0 - not applicable |
Cross-cut test | MAN 0-1 |
Min./max. grip strength | 20-20 min |
Cross-cut test conditions | 0 - not applicable |
Conditions for resistance in salt-spray test | 0 - not applicable |
Shelf life from production | 36 Month |
Conditions to maintain shelf life from production | at 15°C to 25°C |