Silicone acetate, crystal clear
Silicone acetate, crystal clear
SILSEAL-ACE-GLASSCLEAR-310ML
Register now and access more than 150,000 products
- Highly transparent
- Permanently elastic
- Not suitable for applications involving contact with food or for applications in structural glazing, on granite and natural stone
- A glass seam seal is not recommended
- Risk of corrosion when used on bare iron and coloured materials
- Must not be applied to materials that may give off substances or by-products over time e.g. insulating and tar-based paints, butyl sealants or EPDM rubbers. Otherwise this may result in discolouration of the sealant or impaired adhesion.
- Due to the large number of varnish and glazing formulations, always carry out your own tests on the area first, especially on alkyd resin paints and powder-coated aluminium
- Yellowing on contact with white alkyd resin paints cannot be excluded
- Use of a smoothing agent may cause the silicone to become cloudy
- Not to be used in conjunction with pre-compressed sealing tapes
Datasheets(X)
- For sealing in glass, display window, window, display case and furniture construction
- For small-sized bonding, for artistic applications, such as for glass ornaments or glass bricks
- The surface must be load-bearing, clean, dry and free from grease, rust and water
- Do not use in heavy rain
- The joint dimensions must be observed
- Prime the joints with PE back-fill material
- Rework dry before the skin forms as the use of smoothing agent can cause the silicone to become cloudy
- Please observe the "General Notes on Application for Sealants" overview sheet. Further information in the technical data sheet.
Container | Cartridge |
Contents | 310 ml |
Chemical basis | Sauer silicones (acetate systems) |
Colour | Crystal clear |
Continuous motion absorption | 12.5 % |
Shore A hardness | 20 |
Min./max. processing temperature | 5 to 40 °C |
Min./max. temperature resistance | -40 to 150 °C |
Full curing speed/conditions | 3 mm/d / 23°C and 50% relative humidity |
Min. skin-formation time | 15 min |
Conditions for skin-formation time | at 23°C and 50% relative humidity |
Min./max. full curing speed /conditions | 2-3 mm/d / 23°C and 50% relative humidity |
Min. breaking elongation | 150 % |
Fungicidal properties | No |
Building material class | B2 - Normally inflammable |
Shelf life from production | 24 Month |
Building material class/conditions | B2 - Normally inflammable / in accordance with DIN 4102 |
Density/conditions | 1 g/cm³ / at 20°C |
Density | 1 g/cm³ |