Low-strength hydraulic sealant
Low-strength hydraulic sealant
HYDRSEAL-DOS-LOSTRTH-50G
Register now and access more than 150,000 products
Low-strength, therefore to easy disassemble
Excellent resistance to all hydraulic fluids and fuels
High degree of safety, as impairments due to dissolution of the product can be prevented.
Fast curing, even at low temperatures
Minimised downtimes
100 % sealing
Gaps are filled completely, so that the resulting bonding provides protection against corrosion from friction and protection against rust.
Resistant to a large number of bases, gases, solvents, oils and fuels
Silicone-free, solvent-free and oil-free
DOS system:
- Practical, one-hand operation thanks to the practical turn closure, therefore always one hand free to grip with
- Continuously adjustable dispensing system enables dispensing to be adjusted to suit the application and to keep consumption and costs to a minimum
- Costs optimised thanks to emptying with virtually no remaining product in the dispensing neck
- As a result of the powerfully accelerating effect of copper or copper alloys, the sealant can begin to harden during the sealing process. This can cause micro-cracks, which may lead to leaks in the future. We therefore strongly recommend preliminary tests for process assurance if the hydraulic sealant is used in connections containing copper that will come into contact with water ≥ 40°C in the long term. The user is responsible for determining the suitability of the product for the particular application and adhesion process.
- The following plastics can be affected in the event of prolonged exposure: ABS, celluloid, polystyrene, polycarbonate (Macrolon), PMMA (Plexiglas), polysulfone, SAN (lurane, Tyril), Vinidur, vulcanised fibre and painted surfaces.
Datasheets(X)
For sealing pneumatic and hydraulic screw connections up to 200 bar, with prestressed screw connections up to the burst pressure of the pipe/hose. Specially designed for use with high-pressure fluid systems in the automotive and commercial vehicle industry, metal and tool manufacturing, shipbuilding, machine and engine construction, electrical and electronics construction.
This liquid plastic cures when in contact with metal in the absence of oxygen. The contact surfaces must be dry, dust-free and grease-free. Moisten the adhesive surfaces sufficiently and put them together immediately.
For more information, please refer to the technical data sheet.
Chemical basis | Methacrylic acid ether |
Colour | Violet |
Density/conditions | 1.2 g/cm³ / in accordance with DIN EN ISO 2811-1 |
Min./max. viscosity /conditions | 14000-20000 mPas / at 25°C, Brookfield RVT, spindle 2/2.5 rpm |
Max. gap-filling ability | 0.15 mm |
Suitable for | Thread diameter max. R 3/4 inch |
Fully hardening/curing conditions | Exclusion of oxygen and contact with metal (copper or iron ions) |
Min./max. initial strength | 30-40 min |
Min./max. functional strength | 2-3 h |
Min./max. final strength | 12 h-24 h |
Min./max. breakaway torque | 5-10 Nm |
Breakaway torque conditions | DIN EN 15865 |
Min./max prevail torque | 0-3 Nm |
Conditions for prevail torque | DIN EN 15865 |
Min./max. compressive shearing strength /conditions | 1-5 N/mm² / in accordance with ISO 10123 |
Min./max. processing temperature | 5 to 35 °C |
Min./max. temperature conditions | -55 to 150 °C |
Min. flashing point | 100 °C |
Shelf life from production/conditions | 18 Month / at room temperature |
Weight of content | 50 g |
Silicone-free | Yes |
Solvent-free | Yes |