2-component B2 frame foam
2C frame foam B2
DRFRMFM-2C-B2-210ML
Register now and access more than 150,000 products
- Non-chlorinated hydrocarbons
- No formaldehyde or PCB
- Construction class B2 as per DIN 4102
- Pressure and tension-free hardening without being affected by humidity
Datasheets(X)
The surface must be clean, dry and free from loose particles and release agents. Pretreat plaster and gas concrete with primer. Cut off cartridge ends with a knife and apply mixing tube. Also use extension tube for narrow and deep joints. Wear gloves! Do not work with dirty hands/gloves as a general rule. For further details, refer to the technical information leaflet.
Chemical basis | 0 - not applicable |
Colour | Light beige |
Smell/fragrance | 0 - not applicable |
Moulded density | 55 kg/m³ |
Conditions for moulded density | 0 - not applicable |
Cell structure | 0 - not applicable |
Cell structure conditions | 0 - not applicable |
Working life | 0 s |
Tack-free after | 80 s |
Conditions for being tack-free | 0 - not applicable |
Can be cut after | 5 min |
Conditions for ability to cut | 0 - not applicable |
Full resilience | 1 s |
Conditions for full resilience | 0 - not applicable |
Final spreading possible after | 30 min |
Conditions for final spreading | 0 - not applicable |
Min./max. processing temperature | 10 to 60 °C |
Min./max. ambient processing temperature | 10 to 30 °C |
Min./max. surface processing temperature | 5 to 30 °C |
Min./max. processing temperature for can | 10 to 60 °C |
Min./max. temperature resistance | -30 to 80 °C |
Compression strength | 65 kPa |
Compression strength conditions | in accordance with DIN 53421 |
Min. combined tension and shear resistance | 80 kPa |
Conditions for combined tension and shear resistance | 0 - not applicable |
Min. tensile strength | 80 kPa |
Conditions for tensile strength | 0 - not applicable |
Elongation at break | 10 % |
Elongation at break conditions | 0 - not applicable |
Yield (volume) approx. | 4 l |
Conditions for yield | at 20°C |
Contents | 210 ml |
Weight of content | 238 g |
Building material class | B2 - Normally inflammable |
Building material class conditions | in accordance with DIN 4102 |
Resistance against | 0 - not applicable |
Shelf life from production | 9 Month |
Conditions to maintain shelf life from production | at 20°C |